Liu Gaoxiang. THE RELATIONSHIP BETWEEN INNER-EXPANSION VALUES AND WALL FORMATION AMOUNT & D/T RATIO IN THREE-ROLL CROSS ROLLING[J]. STEEL PIPE, 1990, 19(6): 37-40.
Citation:
Liu Gaoxiang. THE RELATIONSHIP BETWEEN INNER-EXPANSION VALUES AND WALL FORMATION AMOUNT & D/T RATIO IN THREE-ROLL CROSS ROLLING[J]. STEEL PIPE, 1990, 19(6): 37-40.
Liu Gaoxiang. THE RELATIONSHIP BETWEEN INNER-EXPANSION VALUES AND WALL FORMATION AMOUNT & D/T RATIO IN THREE-ROLL CROSS ROLLING[J]. STEEL PIPE, 1990, 19(6): 37-40.
Citation:
Liu Gaoxiang. THE RELATIONSHIP BETWEEN INNER-EXPANSION VALUES AND WALL FORMATION AMOUNT & D/T RATIO IN THREE-ROLL CROSS ROLLING[J]. STEEL PIPE, 1990, 19(6): 37-40.
THE RELATIONSHIP BETWEEN INNER-EXPANSION VALUES AND WALL FORMATION AMOUNT & D/T RATIO IN THREE-ROLL CROSS ROLLING
A new method for calculating inner expansion values of tubes rolled by a three-roll mill is put forward based on rolling experiments on a φ108mm three-roll mill, and the metal-flow features in wall compression formation during three-roll cross-rolling are analysed.